Carbon-Bond 61LP Electrically Conductive, Carbon Filled, Long Pot Life Low Gassi

Description

CARBON FILLED ELECTRICALLY CONDUCTIVE EPOXY
PRODUCT DESCRIPTION:
Carbon-Bond 61LP Electrically Conductive, Carbon Filled, Long Pot Life Low Gassing is an epoxy adhesive and coating formulation based on conductive carbon.  This product's chemical formulation allows for micro-thin application and eliminted any air pockets or bubbling between thinly bonded substrates.
Carbon-Bond 61LP Electrically Conductive, Carbon Filled, Long Pot Life Low Gassing is recommended for electronic bonding and sealing applications that require both fine electrical and mechanical properties.
Carbon-Bond 61LP Electrically Conductive, Carbon Filled, Long Pot Life Low Gassing cures at room temperature or can be accelerated with mild heat to form a tenacious bond between similar and dissimilar substrates.
GENERAL PROPERTIES
Appearance
Black
Cure Type
Heat cure or Room temperature
Benefits
Continuity of conductivity
High adhesion
Wide operating temperature range
Mix Ratio by weight
100:12 / Resin:Hardener
Substrates
Aluminum, copper, magnesium, steel, bronze, nickel, ceramic, glass, phenolic, G-10 epoxy glass boards
Operating Temperature
-50 to 170 C
Typical Applications
Electronic bonding and sealing applications that require both fine electrical and mechanical properties.
Shelf Life
6 Months
UNCURED PROPERTIES
Compressive Strength, psi
13,000
Specific Gravity, mixed
1.35 g/cc
Pot Life
3 Hours
CURE SCHEDULE:
15 minutes
@ 100C
1 hour
@ 60C
24 hours
@ 25C
MISC PROPERTIES:
Volume Resistivity
ohm cm: < 40
Tensile Strength, psi
8,500
Shrinkage Linear
0.003 in/in
Hardness, Shore D
85
GENERAL INFORMATION:
For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS).
HOW TO USE:
1) Carefully clean and dry all surfaces to be bonded.
2) Apply AA-CARB 61 completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured.
3) Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.
4) Some ingredients in this formulation provided may crystallize when subjected to low temperature storage. A gentle warming cycle of 52C for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be re-dissolved prior to use for best results.
AVAILABILITY:
This epoxy can be supplied in various different packages.